| POM 500T 美國杜邦公司 物性數(shù)據(jù) |
| 規(guī)格級別： | 注塑級 | 外觀顏色： | --- |
| 用途概述： | 需要較好韌性的一般機械零件。 | ||
| 備注說明： | 加工特性：一般表面潤滑等級。產(chǎn)品特性：韌性與DELRIN 100相近，低磨耗，但剛性與強硬度些微降低。 | ||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.39 | --- |
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.31 | % | |
| 吸水量 | 50%相對濕度 | ASTM D-570 | 0.27 | % | |
| 吸水量 | 浸漬平衡點 | ASTM D-570 | 0.75 | % | |
| 模收縮 | --- | --- | 1.7-1.9 | % | |
| 機械性能 | 洛氏硬度 | --- | ASTM D-785 | 79 | M scale |
| 洛氏硬度 | --- | ASTM D-785 | 117 | R scale | |
| 拉伸強度 | -55℃ | ASTM D-638 | 99 | MPa | |
| 拉伸強度 | 23℃ | ASTM D-638 | 58 | MPa | |
| 拉伸強度 | 70℃ | ASTM D-638 | >38 | MPa | |
| 拉伸強度 | 100℃ | ASTM D-638 | >23 | MPa | |
| 拉伸強度 | 122℃ | ASTM D-638 | >16 | MPa | |
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 22 | % | |
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 91 | % | |
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | >545 | % | |
| 破裂點拉伸變形量 | 100℃ | ASTM D-638 | >585 | % | |
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | >505 | % | |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 2330 | MPa | |
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 3670 | MPa | |
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 2420 | MPa | |
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 1260 | MPa | |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 690 | MPa | |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 420 | MPa | |
| 撓曲變形強度 | 23℃ | ASTM D-790 | 70 | MPa | |
| 壓縮應力 | 23℃,1%變形 | ASTM D-695 | 16 | MPa | |
| 壓縮應力 | 23℃,10%變形 | ASTM D-695 | 82 | MPa | |
| 抗剪強度 | 23℃ | ASTM D-732 | 49 | MPa | |
| 撓曲疲勞忍耐限度 | 50%RH,23℃,106周期 | ASTM D-671 | 25 | MPa | |
| 負載變形量 | 140kg/cm2,50℃ | ASTM D-621 | 0.9 | % | |
| 抗拉伸沖擊強度 | 長試片23℃ | ASTM D-1822 | 835 | kj/m2 | |
| IZOD沖擊試驗 | 缺口-40℃ | ASTM D-256 | 106 | j/m | |
| IZOD沖擊試驗 | 23℃ | ASTM D-256 | 143 | j/m | |
| 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 12.4 | 10-5m/m℃ | |
| 電氣性能 | 抗電弧 | 3.1mm | ASTM D-495 | 120 | sec |
| 介電常數(shù) | 50%RH,23℃,102～106Hz | ASTM D-150 | 3.6 | ohm-cm | |
| 介電因數(shù) | 50%RH,23℃,106Hz | ASTM D-150 | 0.016 | --- | |
| 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 15.1(2.3) | kv/mm | |
| 容積電阻率 | 23℃,0.2%含水量 | ASTM D-257 | 2.3×1015 | Ω.cm | |
| 熱 性 能 | 自燃性 | --- | UL-94 | HB | --- |
| 線性熱膨脹系數(shù) | 104～160℃ | ASTM D-696 | 15.7 | 10-5m/m℃ | |
| 線性熱膨脹系數(shù) | -40～29℃ | ASTM D-696 | 10.2 | 10-5m/m℃ | |
| 線性熱膨脹系數(shù) | 29～60℃ | ASTM D-696 | 12.0 | 10-5m/m℃ | |
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 85 | ℃ | |
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 174 | ℃ | |
| 熔點 | ASTM D-2133 | --- | 175 | ℃ | |