羅地亞PA6 TECHNYL C 216 V30 產(chǎn)品特性：含30%玻璃纖維增強(qiáng)，潤滑，熱性能和機(jī)械性能的良好結(jié)合，用于汽車，電子電氣應(yīng)用等
我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費(fèi)提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權(quán)威資料請致電13268582149
PA6 C216V30 物性表：
| Physical |
Dry |
Conditioned |
Unit |
Test Method |
| Density |
1.35 |
-- |
g/cm³ |
ISO 1183 |
| Density |
1350 |
-- |
kg/m³ |
ISO 1183 2 |
| Water Absorption (23°C, 24 hr) |
0.95 |
-- |
% |
ISO 62 |
| Water Absorption (Equilibrium) |
2.1 |
-- |
% |
ISO 62 2 |
| Mechanical |
Dry |
Conditioned |
Unit |
Test Method |
| Tensile Modulus |
9600 |
6200 |
MPa |
ISO 527-2/1A |
| Tensile modulus |
9600 |
6200 |
MPa |
ISO 527-2 2 |
| Tensile Stress (Break) |
190 |
110 |
MPa |
ISO 527-2/1A |
| Tensile Stress (Break) |
190 |
110 |
MPa |
ISO 527-2 2 |
| Tensile Strain (Break) |
3.8 |
4.5 |
% |
ISO 527-2/1A |
| Tensile Strain (Break) |
3.8 |
4.5 |
% |
ISO 527-2 2 |
| Flexural Modulus |
9500 |
5500 |
MPa |
ISO 178 |
| Impact |
Dry |
Conditioned |
Unit |
Test Method |
| Charpy Notched Impact Strength |
15 |
32 |
kJ/m² |
ISO 179/1eA |
| Charpy notched impact strength (23°C) |
15.0 |
31.5 |
kJ/m² |
ISO 179/1eA 2 |
| Charpy Unnotched Impact Strength |
100 |
110 |
kJ/m² |
ISO 179/1eU |
| Charpy impact strength (23°C) |
100 |
108 |
kJ/m² |
ISO 179/1eU 2 |
| Notched Izod Impact Strength |
14 |
24 |
kJ/m² |
ISO 180/1A |
| Thermal |
Dry |
Conditioned |
Unit |
Test Method |
| Deflection Temperature Under Load (0.45 MPa) |
217 |
-- |
°C |
ISO 75-2 2 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) |
205 |
-- |
°C |
ISO 75-2/Af |
| Deflection Temperature Under Load (1.8 MPa) |
205 |
-- |
°C |
ISO 75-2 2 |
| Glass Transition Temperature 3 |
55 |
-- |
°C |
ISO 11357-2 2 |
| Melting Temperature (DSC) |
222 |
-- |
°C |
ISO 3146 |
| Melting Temperature 3 |
222 |
-- |
°C |
ISO 11357-3 2 |
| CLTE - Flow |
0.000032 |
-- |
cm/cm/°C |
ISO 11359-2 2 |
| CLTE - Transverse (23 to 85°C) |
0.000032 |
-- |
cm/cm/°C |
ISO 11359-2 |
| Electrical |
Dry |
Conditioned |
Unit |
Test Method |
| Surface Resistivity |
1.0E+13 |
1.0E+11 |
ohms |
IEC 60093 |
| Surface resistivity |
-- |
1.0E+11 |
ohms |
IEC 60093 2 |
| Volume Resistivity |
1.0E+15 |
1.0E+11 |
ohm·cm |
IEC 60093 |
| Volume resistivity |
1.0E+13 |
1.0E+9 |
ohm·m |
IEC 60093 2 |
| Relative Permittivity (1 MHz) |
3.80 |
4.50 |
|
IEC 60250 2 |
| Dissipation Factor |
0.020 |
0.090 |
|
IEC 60250 |
| Dissipation Factor (1 MHz) |
0.020 |
0.090 |
|
IEC 60250 2 |
| Comparative Tracking Index (Solution A) |
550 |
475 |
V |
IEC 60112 |