性能項目
|
試驗條件[狀態(tài)]
|
測試方法
|
測試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
|
基本性能
|
熔體流動速率
|
/
|
ASTM D-1238
|
2.5
|
G/10min
|
|
VA含量
|
/
|
/
|
18
|
%
|
|
|
密度
|
/
|
ASTM D-1505
|
0.938
|
g/cm3
|
|
|
機械性能
|
拉力斷裂強度
|
/
|
ASTM D-638
|
150
|
%
|
|
彎曲模量
|
/
|
ASTM D-790
|
150
|
kg/cm2
|
|
|
硬度
|
/
|
ASTM D-2240
|
88
|
kg/cm2
|
|
|
拉力降伏強度
|
/
|
ASTM D-638
|
45
|
kg/cm2
|
|
|
拉力斷裂伸長率
|
/
|
ASTM D-638
|
800
|
kg/cm2
|
|
|
硬度
|
/
|
ASTM D-2240
|
38
|
Shore D
|
|
|
熱 性 能
|
軟化點
|
/
|
ASTM D-1525
|
60
|
℃
|
|
熔點
|
/
|
DSC
|
84
|
℃
|
|
|
脆化溫度
|
/
|
ASTM D-746
|
<-70
|
℃
|
|