性能項(xiàng)目
|
測(cè)試方法
|
測(cè)試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
熔體流動(dòng)速率
|
ASTM D-1238
|
1.0
|
g/10min
|
|
熔點(diǎn)
|
HPC
|
94
|
℃
|
|
斷裂拉伸強(qiáng)度
|
ASTM D-638
|
21.56
|
MPa
|
|
斷裂伸長(zhǎng)率
|
ASTM D-638
|
650
|
%
|
|
肖氏硬度
|
ASTM D-2240
|
46
|
|
|
拉伸模量
|
ASTM D-638
|
40
|
MPa
|
|
落球沖擊強(qiáng)度
|
ASTM D-1709A
|
＞400
|
g
|
|
斷裂伸長(zhǎng)率
|
ASTM D-882
|
400
|
%
|
|
維卡軟化點(diǎn)
|
ASTM D-1525
|
85
|
℃
|
|
VA含量
|
HPC
|
9
|
wt.%
|
|
密度
|
ASTM D-1505
|
0.930
|
g/cm3
|
|
薄膜厚度
|
HPC
|
60
|
μm
|
|
霧度
|
ASTM D-1003
|
4.5
|
%
|
|
光澤度
|
ASTM D-2457
|
100
|