| PA6T CH230N 三井化學株式會社 物性數據 |
| 暫無此原料描述部分┄ |
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 吸水率 | 23℃,24小時在水里(2mmt,100℃) | ASTM D-570 | 0.3(3.0) | % |
| 物理性能 | 模具收縮率 | 2mmt | ASTM D-955 | 0.4(0.8) | % |
| 比重 | --- | ASTM D-792 | 1.63 | --- | |
| 機械性能 | 拉伸強度 | dry(moist) | ASTM D-638 | 160(140) | MPa |
| 拉伸伸長率 | dry(moist) | ASTM D-638 | 4(3) | % | |
| 彎曲強度 | dry(moist) | ASTM D-790 | 240(200) | MPa | |
| 彎曲模量 | dry(moist) | ASTM D-790 | 11000(8000) | MPa | |
| IZOD缺口沖擊強度 | dry(moist) | ASTM D-256 | 80(90) | J/M | |
| 洛氏硬度 | --- | ASTM D-785 | 95 | M scale | |
| 電氣性能 | 體積電阻率 | dry | ASTM D-257 | 1015 | Ω.cm |
| 介電常數 | 1016Hz,dry | ASTM D-150 | 4.0 | --- | |
| 損耗因數 | 1016Hz,dry | ASTM D-150 | 25 | --- | |
| Dielectric breakdown voltage | dry | ASTM D-149 | 25 | KV/mm | |
| 熱 性 能 | 熔點 | --- | --- | 310 | ℃ |
| 玻璃轉變溫度 | --- | --- | 85 | ℃ | |
| 負荷撓曲溫度 | --- | ASTM D-648 | 290 | ℃ | |
| 線性熱膨脹系數 | --- | ASTM D-696 | 3.0(6.0) | ×10-5/℃ | |
| 阻燃性 | --- | UL 94 | V-0 | --- | |
| 其它性能 | Glass fiber content | --- | --- | 30 | % |